Characteristics
- Extrusion/Injection
- Medium to High Impact Strength
- Good Processablity, good flow
- High Gloss
Applications
- Computer / TV / Telephone housing
- Toys
- Furniture
- Digital products shell
- Extruded Film
- Office equipments
- Kitchen appliances
- Daily house ware
- Battery cases
- Shoe heels
| Property |
ASTM |
Test Conditions |
Metric system |
English units |
| Unit |
Property |
Unit |
Property |
| Mechanical |
|
|
|
|
|
|
| Izod Impact Strength |
ASTMD256 |
23°C , 1/2 inch, notched |
kg-cm/cm |
21 |
ft-lb/in |
3.9 |
| Izod Impact Strength |
ASTMD256 |
23°C , 1/8 inch, notched |
kg-cm/cm |
27 |
ft-lb/in |
4.9 |
| Tensile strength at yield |
ASTMD638 |
23°C , 1/8 inch , 5 mm/min |
kg/cm 2 |
430 |
psi |
6100 |
| Tensile strength at break |
ASTMD638 |
23°C , 1/8 inch, 5 mm/min |
kg/cm 2 |
350 |
psi |
5000 |
| Elongation at Break |
ASTMD638 |
23°C , 1/8 inch, 5 mm/min |
% |
30 |
|
|
| Flexural Yield |
ASTMD790 |
23°C , 2.8 mm/min |
kg/cm 2 |
700 |
psi |
10000 |
| Flexural Modulus |
ASTMD790 |
23°C , 2.8 mm/min |
kg/cm 2 |
24000 |
psi |
340000 |
|
|
|
|
|
|
|
| Thermal |
|
|
|
|
|
|
| Heat Distortion Temp. |
ASTMD648 |
unanealed, 1/2 inch, 18.56 kg/cm 2 load |
°C |
87 |
°F |
189 |
| Vicat Softening Temp. |
ASTMD1525 |
1/8 inch, 1kg load |
°C |
102 |
°F |
216 |
|
|
|
|
|
|
|
| Physical Property |
|
|
|
|
|
|
| Specific Gravity |
ASTMD792 |
|
|
1.03 |
|
|
| Rockwell Hardness |
ASTMD785 |
23°C , R-scale |
R-scale |
110 |
|
|
| Mold Shrinkage |
ASTMD955 |
|
% |
? 0.4 |
|
|
| Water Absorption |
ASTMD570 |
|
wt % |
? 0.3 |
|
|
| Melt Flow Index |
ASTMD1238 |
200 °C , 5kg load |
g/10min |
2.0 |
|
|
| Melt Flow Index |
ASTMD1238 |
220°C , 10kg load |
g/10min |
18 |
|
|
|
|
|
|
|
|
|
| Flammability |
UL-94 |
1/16 inch |
File No E50263 |
HB |
|
|
|
|
|
|
|
|
|
| Electrical |
|
|
|
|
|
|
| Relative Temp. Index(RTI) |
UL-764B |
0.062 inch plus |
°C |
60 |
°F |
140 |
| Hot wire Ignition(HWI) |
UL-764A |
0.062 inch plus |
Secs |
17 |
|
|
| High Current Arc Ignition(HCAI) |
UL-764A |
0.062 inch plus |
Arcs |
200 |
|
|
| Arc Tracking Rate(ATR) |
UL-764A |
0.062 inch plus |
in/min |
0 |
|
|
Note1: Laboratory testing result. It is not the test result of contracted products.
Note2: Property of dyed products are as same as the natural product. |
|