Characteristics
- Extrusion/Injection
- High Impact Strength
- Good Processablity, good flow
- High productivity
Applications
- Digital Products shells
- Shoe heels
- Large or complex shaped products
- Vacuum machine
- Air conditioner surface
- Cash registers
Property |
ASTM |
Test Conditions |
Metric system |
English units |
Unit |
Property |
Unit |
Property |
Mechanical |
|
|
|
|
|
|
Izod Impact Strength |
ASTMD256 |
23°C, 1/2 inch, notched |
kg-cm/cm |
26 |
ft-lb/in |
4.7 |
Izod Impact Strength |
ASTMD256 |
23°C, 1/8 inch, notched |
kg-cm/cm |
29 |
ft-lb/in |
5.2 |
Tensile strength at yield |
ASTMD638 |
23°C, 1/8 inch, 5 mm/min |
kg/cm 2 |
380 |
psi |
5400 |
Tensile strength at break |
ASTMD638 |
23°C, 1/8 inch, 5 mm/min |
kg/cm 2 |
340 |
psi |
4900 |
Elongation at Break |
ASTMD638 |
23°C, 1/8 inch, 5 mm/min |
% |
20 |
|
|
Flexural Yield |
ASTMD790 |
23°C, 2.8 mm/min |
kg/cm 2 |
670 |
psi |
9600 |
Flexural Modulus |
ASTMD790 |
23°C, 2.8 mm/min |
kg/cm 2 |
25000 |
psi |
360000 |
|
|
|
|
|
|
|
| Thermal |
|
|
|
|
|
|
Heat Distortion Temp. |
ASTMD648 |
unanealed, 1/2 inch, 18.56 kg/cm 2 load |
°C |
84 |
°F |
183 |
Vicat Softening Temp. |
ASTMD1525 |
1/8 inch, 1kg load |
°C |
98 |
°F |
205 |
|
|
|
|
|
|
|
| Physical Property |
|
|
|
|
|
|
Specific Gravity |
ASTMD792 |
|
|
1.03 |
|
|
Rockwell Hardness |
ASTMD785 |
23°C, R-scale |
R-scale |
108 |
|
|
Mold Shrinkage |
ASTMD955 |
|
% |
? 0.4 |
|
|
Water Absorption |
ASTMD570 |
|
wt % |
? 0.3 |
|
|
Melt Flow Index |
ASTMD1238 |
200°C , 5kg load |
g/10min |
5.0 |
|
|
Melt Flow Index |
ASTMD1238 |
220°C , 10kg load |
g/10min |
41.0 |
|
|
|
|
|
|
|
|
|
| Flammability |
UL-94 |
1/16 inch |
File No E50263 |
HB |
|
|
|
|
|
|
|
|
|
| Electrical |
|
|
|
|
|
|
Relative Temp. Index(RTI) |
UL-764B |
0.062 inch plus |
°C |
- |
°F |
- |
Hot wire Ignition(HWI) |
UL-764A |
0.062 inch plus |
Secs |
- |
|
|
High Current Arc Ignition(HCAI) |
UL-764A |
0.062 inch plus |
Arcs |
- |
|
|
Arc Tracking Rate(ATR) |
UL-764A |
0.062 inch plus |
in/min |
- |
|
|
Note1: Laboratory testing result. It is not the test result of contracted products.
Note2: Property of dyed products are as same as the natural product.
|
|