Characteristics
- Injection
- Medium level impact strength
- Easy process, high melt flow
- High gloss
- High rigidity
Applications
- Tape recorder / video Cassettes
- Clock
- House-ware appliances
- Digital product shell
- Office equipments
- Daily use products
Property |
ASTM |
Test Conditions |
Metric system |
English units |
Unit |
Property |
Unit |
Property |
Mechanical |
|
|
|
|
|
|
Izod Impact Strength |
ASTMD256 |
23°C, 1/2 inch, notched |
kg-cm/cm |
13 |
ft-lb/in |
2.4 |
Izod Impact Strength |
ASTMD256 |
23°C, 1/8 inch, notched |
kg-cm/cm |
16 |
ft-lb/in |
2.9 |
Tensile strength at yield |
ASTMD638 |
23°C, 1/8 inch, 5 mm/min |
kg/cm 2 |
480 |
psi |
6800 |
Tensile strength at break |
ASTMD638 |
23°C, 1/8 inch, 5 mm/min |
kg/cm 2 |
380 |
psi |
5400 |
Elongation at Break |
ASTMD638 |
23°C, 1/8 inch, 5 mm/min |
% |
20 |
|
|
Flexural Yield |
ASTMD790 |
23°C, 2.8 mm/min |
kg/cm 2 |
800 |
Psi |
11400 |
Flexural Modulus |
ASTMD790 |
23°C, 2.8 mm/min |
kg/cm 2 |
30000 |
Psi |
420000 |
|
|
|
|
|
|
|
| Thermal |
|
|
|
|
|
|
Heat Distortion Temp. |
ASTMD648 |
unanealed, 1/2 inch, 18.56 kg/cm 2 load |
°C |
89 |
°F |
192 |
Vicat Softening Temp. |
ASTMD1525 |
1/8 , 1kg load |
°C |
104 |
°F |
219 |
|
|
|
|
|
|
|
| Physical Property |
|
|
|
|
|
|
Specific Gravity |
ASTMD792 |
|
|
1.04 |
|
|
Rockwell Hardness |
ASTMD785 |
23°C, R-scale |
R-scale |
119 |
|
|
Mold Shrinkage |
ASTMD955 |
|
% |
<= 0.4 |
|
|
Water Absorption |
ASTMD570 |
|
wt % |
<= 0.3 |
|
|
Melt Flow Index |
ASTMD1238 |
200, 5kg load |
g/10min |
2.3 |
|
|
Melt Flow Index |
ASTMD1238 |
220°C, 10kg load |
g/10min |
23.0 |
|
|
|
|
|
|
|
|
|
| Flammability |
UL-94 |
1/16 inch |
File No E50263 |
HB |
|
|
|
|
|
|
|
|
|
| Electrical |
|
|
|
|
|
|
Relative Temp. Index(RTI) |
UL-764B |
0.062 inch plus |
°C |
60 |
°F |
140 |
Hot wire Ignition(HWI) |
UL-764A |
0.062 inch plus |
Secs |
15 |
|
|
High Current Arc Ignition(HCAI) |
UL-764A |
0.062 inch plus |
Arcs |
15 |
|
|
Arc Tracking Rate(ATR) |
UL-764A |
0.062 inch plus |
in/min |
0 |
|
|
Note1: Laboratory testing result. It is not the test result of contracted products.
Note2: Property of dyed products are as same as the natural product.
|
|