| Wlasnosci |
Metoda Badania |
Warunki |
Jednostka |
W³a¶ciwo¶ci |
| Mechaniczne |
|
|
|
|
| Udarnosc z karbem Izoda |
ASTMD256 |
23 °C , 1/2 inch, notched |
kg-cm/cm |
16 |
| Udarnosc z karbem Izoda |
ASTMD256 |
23 °C , 1/8 inch, notched |
kg-cm/cm |
20 |
| Modul sprezystosci przy rozciag |
ASTMD638 |
23 °C , 1/8 inch , 5 mm/min |
kg/cm2 |
440 |
| Granica Plastycznosci |
ASTMD638 |
23 °C , 1/8 inch, 5 mm/min |
kg/cm2 |
390 |
| Wydluzenie przy zerwaniu |
ASTMD638 |
23 °C , 1/8 inch, 5 mm/min |
% |
20 |
| Naprezenie zginajace |
ASTMD790 |
23 °C , 2.8 mm/min |
kg/cm2 |
760 |
| Modul sprezystosci zginania |
ASTMD790 |
23 °C, 2.8 mm/min |
kg/cm2 |
27000 |
|
|
|
|
|
| Termiczne |
|
|
|
|
| Temperatura ugiecia pod obciazeniem. |
ASTMD648 |
unanealed, 1/2 inch, 18.56 kg/cm2 load |
°C |
85 |
| Temperatura miekniecia Vicat |
ASTMD1525 |
1/8 inch, 1kg load |
°C |
100 |
|
|
|
|
|
| Fizyczne |
|
|
|
|
| Gestosc |
ASTMD792 |
|
|
1.04 |
| Twardosc met. wciskania kulki |
ASTMD785 |
23 °C , R-scale |
R-scale |
118 |
| Skurcz liniowy |
ASTMD955 |
|
% |
<=0.4 |
| Chlonnosc wody |
ASTMD570 |
|
wt % |
<=0.3 |
| Lepkosc wzgledna |
ASTMD1238 |
200°C , 5kg load |
g/10min |
4.5 |
| Lepkosc wzgledna |
ASTMD1238 |
220 °C , 10kg load |
g/10min |
40.0 |
|
|
|
|
|
| Palnosc |
UL-94 |
1/16 inch |
File No E50263 |
HB |
|
|
|
|
|
| Elektryczne |
|
|
|
|
| Wspólczynnik temp. wzglednej |
UL-764B |
0.062 inch plus |
? |
60 |
| Zaplon przy goracym przew. |
UL-764A |
0.062 inch plus |
Secs |
14 |
| Zaplon przy wysokim natezeniu pradu |
UL-764A |
0.062 inch plus |
Arcs |
200 |
| Pe³zanie p³omienia |
UL-764A |
0.062 in above |
in/min |
0 |
|
|
|
|
|
| Note1: Laboratory testing result. It is not the test result of contracted products. |
|
| Note2: Property of dyed products are as same as the natural product. |